Pneumatic tire with electrically conductive cord extending between a bead portion and a tread portion of the tire

ABSTRACT

A pneumatic rubber tire containing at least one electrically conductive cord extending between its bead and tread portions to provide a path of least electrical resistance. The electrically conductive cord is comprised of at least one electrically conductive metal filament spirally wound around a centrally disposed core of at least one organic fiber. The electrically conductive cord does not extend to, and is exclusive of, an outer surface of the tire.

This application claims the benefit of Provisional Application Ser. No. 60/513,738 filed Oct. 23, 2003.

FIELD OF THE INVENTION

This invention relates to a pneumatic rubber tire which contains at least one electrically conductive cord extending between its electrically conductive wheel-rim mounting surface rubber component and its electrically conductive tread base layer rubber component or one or more intermediate electrically conductive rubber components therebetween to provide a path of least electrical resistance between the tire wheel-rim mounting surface and the tire tread base layer. An electrically conductive path is thereby provided. The electrically conductive cord is comprised of at least one electrically conductive metal filament spirally wound around a centrally disposed core of at least one organic fiber. The electrically conductive cord does not extend to, and therefore is exclusive of, an outer surface of the tire. The electrically conductive cord may also be comprised of an electrically conductive metal filament, electrically conductive carbon fiber, or their combination, spirally wound around a core of at least one organic fiber.

BACKGROUND OF THE INVENTION

Pneumatic rubber tires conventionally have sidewall components which are positioned between at least one bead region of the tire and the tread region of the tire. The tread component of the tire is designed to provide a running surface of the tire for ground-contacting purposes. A wheel-rim mounting surface is conventionally provided in the bead region of the tire which is designed contact a rigid metal rim onto which the tire is mounted to create a tire/wheel assembly.

The bead region of the tire normally includes a rubber encapsulated essentially inextensible bead composed of a bundle of wire cords. The bead region of the tire also normally includes at least one rubber component having a tire mounting surface, for example a chafer and/or toe guard component, of a rubber composition which is designed to be rim-contacting, and therefore a mounting surface of the tire. Such mounting surface rubber composition conventionally contains a significant rubber reinforcing carbon black content and is thereby relatively electrically conductive. Such tire bead region with associated rubber component(s) are well known to those having skill in such art.

The tire tread may be of a cap/base layered construction with the outer cap layer having a running surface of the tire designed to be ground-contacting. The tread base layer underlies and supports the outer tread cap layer and designed to be a transition between the outer tread cap layer and tire carcass plies or tire belt plies. Such tread base layer is conventionally of a rubber composition reinforced with a significant rubber reinforcing carbon black content to be relatively electrically conductive. Such tire tread cap/base construction is well known to those having skill in such art.

A tire may often contain a circumferential belt ply positioned between the tread base layer and the tire carcass plies. Such belt ply is normally composed of metal cords of twisted, or cabled, metal filaments wherein the metal cords are encompassed by a rubber composition (e.g. a rubber wire coat) which is reinforced with a significant rubber reinforcing carbon black content to be relatively electrically conductive. Such belt ply positioning and construction is well known to those having skill in such art.

The tire carcass itself is normally composed of one or more plies of cords encompassed by a rubber composition which usually contains only a more minimal rubber reinforcing carbon black content so that it is thereby relatively electrically nonconductive as compared to said bead region components, tire tread base layer and belt ply rubber. However, for this invention, the rubber composition for a carcass ply, if desired, may be provided as being electrically conductive by inclusion of a significant carbon black content. The carcass ply(ies) typically extend from bead-to-bead through a crown region of the tire. Such carcass ply(ies) construction of the tire is well known to those having skill in such art. The crown region of the tire is the portion of the tire which includes the portion of the tire carcass beneath the tire tread region as the carcass ply(ies) passes from one bead region to the other bead region of the tire as one having skill in such art would understand.

Conventionally, the outer visible rubber layer of the tire sidewalls is of a rubber composition which is reinforced with a significant rubber reinforcing carbon black content so it is relatively electrically conductive in a manner that a suitable path of least electrical resistance is thereby provided to promote dissipation of static electricity from the bead region of the tire (from its wheel-rim mounting surface rubber component) to the tread region with its running surface.

For some applications, however, it may be desired to reduce the carbon black content of the tire outer sidewall layer to, in turn, reduce its hysteresis and thereby make it less hysteretic. A lower hysteretic tire sidewall rubber layer promotes a lower rolling resistance and/or lower heat build up for the respective tire with an associated beneficial increase in fuel economy for an associated vehicle and/or durability of the tire itself. Typically, an increase in the rubber composition's rebound value is indicative of reduced hysteresis if the rubber composition. In practice, a reduction of the carbon black content of the sidewall rubber composition may be accomplished by replacing a portion of the carbon black amorphous silica reinforcement (e.g. a precipitated silica).

However, such reduction in carbon black content in the outer sidewall layer can also significantly reduce the electrical conductivity of the tire sidewall layer, particularly if the carbon black content is reduced below its percolation point, which, in turn, can result in significantly reducing or even eliminating the aforesaid path of suitable electrical conductivity between the tire's bead region and the tire's tread region.

In one aspect, it is desired to provide a tire having an outer, visible tire sidewall layer of a rubber composition having a relatively low carbon black content to an extent that the tire sidewall rubber layer is relatively electrically nonconductive.

For this invention, an electrically conductive cord is provided to provide a path of least electrical resistance between the tire bead region and tire tread region. The cord is provided as a metal filament spirally (helically) wound around a core of one or more organic filaments. The significance of using a spirally wound metal filament is to enable the relatively inextensible metal filament to be dynamically extended and flexed, because of its helically coiled configuration, during the working of the tire and to thereby reduce its fatigue. The organic fiber is used to provided a supporting core substrate for the helically wound metal filament. The electrically conductive cord may also be comprised of an electrically conductive metal filament, electrically conductive carbon fiber or their combination, spirally wound around a core of at least one organic filament.

In the description of this invention, the term “phr” relates to parts by weight of an ingredient per 100 parts by weight of rubber, unless otherwise indicated.

The terms “rubber” and “elastomer” are used interchangeably unless otherwise indicated. The terms “vulcanized” and “cured” are used interchangeably unless otherwise indicated. The terms “compound” and “rubber composition” may be used interchangeably unless indicated. The term “carbon black” is used to refer to rubber reinforcing carbon blacks unless otherwise indicated. Exemplary rubber reinforcing carbon blacks may be referred to, for example, in the Vanderbilt Rubber Handbook(1978) on Pages 414 through 417.

DISCLOSURE AND PRACTICE OF THE INVENTION

In accordance with this invention, a pneumatic rubber tire of open torroidal shape is comprised of:

(A) a tire tread portion comprised of:

-   -   (1) a circumferential rubber tread of a cap/base layered         construction wherein said tread cap rubber layer has an outer         tire tread running surface and said tread base rubber layer         underlies said tread cap layer, and     -   (2) a circumferential belt ply layer underlying said         circumferential tread wherein said belt ply layer is comprised         of steel cords encompassed by a rubber composition (sometimes         referred to as a wire coat rubber composition) contiguous with         said tread base rubber layer;

(B) two spaced apart bead regions individually comprised of:

-   -   (1) a bead portion comprised of relatively inextensible steel         cords encompassed by a rubber composition, and     -   (2) an additional bead portion comprised of at least one rubber         component wherein at least one of said additional bead portion         rubber components has a mounting surface (a wheel-rim mounting         surface) adapted for mounting said tire on a rigid metal rim,

(C) at least one carcass ply comprised of a cord reinforced carcass ply rubber composition wherein at least one of said carcass plies extends from one bead portion to the other bead portion through the crown region of the tire,

(D) a tire rubber inner liner layer positioned on the inside surface of an inner carcass ply (to resist permeation of air from the air cavity of the tire into its carcass),

(E) two outer tire rubber sidewall layers individually extending between said bead region and said tread, and

(F) at least one electrically conductive cord comprised of at least one electrically conductive metal filament spirally wound around a core of at least one organic fiber, wherein said electrically conductive cord extends from at least one of said bead region additional rubber components as said rubber component having a wheel-rim tire mounting surface and/or at least one intermediate rubber composition contiguous with said wheel-rim mounting surface containing rubber component, to said tread rubber base layer, and/or said rubber of said circumferential belt ply

wherein the electrically conductive cord may also be comprised of an electrically conductive metal filament, electrically conductive carbon fiber, or their combination, spirally wound around a core of at least one organic fiber;

wherein said electrically conductive cord is positioned

-   -   (1) on the outer surface of a carcass ply between said carcass         ply and said sidewall rubber layer, or     -   (2) on the inner surface of a carcass ply between said carcass         ply and said tire rubber innerliner layer, or     -   (3) between two carcass plies, or     -   (4) as a member of said cords of at least one of said carcass         plies;

provided, however, that when said electrically conductive cord is positioned on the surface of a carcass ply between two carcass plies or between a carcass ply and tire innerliner layer, or as a member or the cords of a carcass ply,

-   -   -   (a) the said tread base layer, said tread belt ply, said             tire bead composite, and said additional bead component, and             said carcass ply(ies) are relatively electrically conductive             by being comprised of carbon black-rich, rubber based rubber             compositions having a relatively high electrical             conductivity, and         -   (b) the said outer sidewall rubber layer is:             -   (1) relatively electrically conductive, (e.g. comprised                 of a carbon black rich rubber composition), or             -   (2) relatively electrically non-conductive (e.g.                 comprised of a rubber composition which contains only a                 minimal carbon black content or contains no carbon                 black); or

    -   provided however that when said electrically conductive cord is         positioned on the surface of a carcass ply between a carcass ply         and said outer sidewall layer,         -   (c) the said tread base layer, tread belt ply, tire bead             composite and additional bead component are relatively             electrically conductive by being comprised of carbon             black-rich rubber compositions having a relatively high             electrical conductivity, and         -   (d) at least one of said carcass ply(ies) and/or said outer             sidewall rubber layer is:             -   (1) relatively electrically conductive, (e.g. comprised                 of a carbon black rich rubber composition), or             -   (2) relatively electrically non-conductive (e.g.                 comprised of a rubber composition which contains only a                 minimal carbon black content or contains no carbon                 black);

    -   wherein the rubber composition of said tire tread rubber cap         layer         -   (e) is comprised of a carbon black-rich diene rubber based             rubber composition (thereby having a relatively high             electrical conductivity), or         -   (f) is comprised of a diene rubber based rubber composition             which contains a more minimal carbon black content (and             thereby has a relatively low electrical conductivity);             wherein a thin carbon black-rich rubber strip thereby having             a relatively high electrical conductivity is positioned             through or around said tread cap layer having the more             minimal carbon black content and wherein said thin rubber             strip extends from, and as a part of, said tread base rubber             layer to at least a portion of the running surface of said             tread cap layer;

    -   wherein the rubber composition of said outer rubber sidewall         layer contains reinforcing filler as:         -   (g) from about 50 to about 65 phr of rubber reinforcing             carbon black, (considered herein as being relatively             electrically conductive), or         -   (h) from about 25 to about 40 phr of rubber reinforcing             carbon black (considered herein as being relatively             electrically non-conductive), or         -   (i) from about 25 to about 65 phr of amorphous, precipitated             silica and from zero to 10 phr of rubber reinforcing carbon             black (considered herein as being relatively electrically             nonconductive), or         -   (j) about 40 to about 70 phr of reinforcing filler as;             -   (1) about 25 to about 40 phr of amorphous, precipitated                 silica and             -   (2) about 25 to about 35 phr of rubber reinforcing                 carbon black (considered herein as being relatively                 non-electrically conductive);

    -   wherein a coupling agent is provided for said amorphous silica         which has a moiety reactive with hydroxyl groups (e.g. silanol         groups) contained on said amorphous silica and another moiety         interactive with said diene-based elastomer(s);

    -   wherein said carbon black for said rubber sidewall layer has a         dibutyl phthalate (DBP) value (ASTM D2414) in a range of from         about 115 to about 125 cm³/100 g together with an Iodine value         (ASTM D1510) in a range of from about 35 to about 50 ml/100 g;

    -   wherein the rubber composition of said carcass ply(ies) contains         reinforcing filler as:         -   (k) about 45 to about 70, alternately about 50 to about 65,             phr of rubber reinforcing carbon black, (and is therefore             considered herein as being relatively electrically             conductive), or         -   (l) from 25 to about 60 phr of reinforcing filler as;             -   (1) from 5 to about 35 phr of carbon black, and             -   (2) about 15 to about 55 phr of amorphous, precipitated                 silica together with a coupling agent for said silica                 (and is therefore considered

    -   wherein as being relatively electrically non-conductive);

    -   wherein said carbon black has a dibutyl phthalate (DBP) value         (ASTM D2414) in a range of from about 70 to about 110 cm³/100 g         together with an Iodine value (ASTM D1510) in a range of from         about 30 to about 80 ml/100 g;

    -   wherein the rubber composition for said tread rubber cap layer         contains reinforcing filler as:         -   (m) about 45 to about 110 phr of rubber reinforcing carbon             black, (and is therefore considered herein as being             relatively electrically conductive), or         -   (n) from 45 to about 105 phr of reinforcing filler as;             -   (1) from 5 to about 25 phr of carbon black, and             -   (2) about 40 to about 100 phr of amorphous, precipitated                 silica together with a coupling agent for said silica                 (and is therefore considered herein as being relatively                 electrically non-conductive);

    -   wherein said carbon black has a dibutyl phthalate (DBP) value         (ASTM D2414) in a range of from about 110 to about 130 cm³/100 g         together with an Iodine value (ASTM D 1510) in a range of from         about 85 to about 150 ml/100 g;

    -   wherein the rubber composition for said thin rubber strip         extending through or around said tread rubber cap layer is of a         carbon black-rich rubber composition, containing about 50 to         about 75 phr of rubber reinforcing carbon black having a dibutyl         phthalate (DBP) value in a range of from about 100 to about 130         cm³/100 g together with an Iodine value in a range of from about         90 to about 125 ml/100 g;

    -   wherein the said rubber composition(s) of said bead portion         component(s) having the said tire mounting surface contain from         about 60 to about 125 phr of rubber reinforcing carbon black         having a dibutyl phthalate (DBP) value in a range of from about         70 to about 125 cm³/100 g together with an Iodine value in a         range of from about 80 to about 145 ml/100 g, (and is therefore         considered herein as being relatively electrically conductive);

    -   wherein the rubber composition of said belt ply contains from         about 55 to about 75 phr of rubber reinforcing carbon black         having a dibutyl phthalate (DBP) value in a range of from about         65 to about 85 cm³/100 g together with an Iodine value in a         range of from about 75 to about 95 ml/100 g, (and is therefore         considered herein as being relatively electrically conductive);

    -   wherein the rubber composition of said tire tread rubber base         layer contains from about 50 to about 70 phr of rubber         reinforcing carbon black having a dibutyl phthalate (DBP) value         in a range of from about 90 to about 125 cm³/100 g together with         an Iodine value in a range of from about 40 to about 95 ml/100         g, (and is therefore considered herein as being relatively         electrically conductive);

    -   wherein the rubber composition of said tire inner liner layer         contains from about 55 to about 80 phr of rubber reinforcing         carbon black having a dibutyl phthalate (DBP) value in a range         of from about 85 to about 95 cm³/100 g together with an Iodine         value in a range of from about 30 to about 45 ml/100 g, (and is         therefore considered herein as being relatively electrically         conductive).

In practice, it is recognized that the helically wound wire of the said electrically conductive cord (e.g. stainless steel or copper or brass wire for example) would have an electrical resistance of only a few ohms and significantly less than 100 ohms resistance, depending somewhat how tightly the wire is wound around the core, the selection of the wire composition (e.g. stainless steel) and the length of the electrically conductive cord itself.

In practice, preferably the rubber compositions of said individual tire bead component(s), said tire tread rubber base layer, said tire belt ply, said optional relatively electrically conductive tread rubber cap layer, said optional relatively electrically conductive outer sidewall layer, and said optional thin rubber strip extending through or around said tread rubber cap layer contains a rubber reinforcing carbon black content of at least 40 phr, depending somewhat upon the selection of the rubber reinforcing carbon black itself as hereinbefore addressed, and in a sufficient amount that is above the carbon black percolation point to thereby make the rubber composition relatively electrically conductive. The term “percolation point” is well known to those having skill in such art.

It is considered herein that said rubber components of said bead portion, said tire tread rubber base layer, said rubber of said belt ply, said relatively electrically conductive tread rubber cap layer, said thin rubber strip extending through or around said tread rubber cap layer, and optionally said outer rubber sidewall layer, are relatively electrically conductive because of a combination of their rubber reinforcing carbon black contents combined with the characterization of the carbon blacks in terms of their DBP and Iodine values.

It is considered herein that said rubber of said carcass plies, tire innerliner layer, and optionally said outer rubber sidewall layer, are relatively electrically non-conductive (relative to said tire bead rubber components, said tire tread rubber base layer, rubber of said belt ply, said relatively electrically conductive tread rubber cap layer and said thin rubber strip extending through or around said tread rubber cap layer) because of a combination of their limited rubber reinforcing carbon black contents combined with the characterization of the carbon blacks in terms of their DBP and Iodine values.

Representative examples of rubber reinforcing carbon blacks, as represented in The Vanderbilt Rubber Handbook, 1978, Page 417, are, for example, according to their ASTM designations:

For said tire bead region rubber components, including said additional bead region rubber components: N660, N550, N375, N236 and N234;

For said tire tread rubber base layer: N660, N555, N375 and N347;

For said rubber of said belt ply: N347, N330 and N326;

For said tread rubber cap layer: N375, N234, N220, N134, N121, N115 and N110;

For said thin rubber strip which optionally extends through or around said tread rubber cap layer: N375, N347 and N234;

For said carcass ply rubber: N660, N550 and N326;

For said tire inner liner layer: N660; and

For said tire outer sidewall rubber layer: N550, N660, N375, N330 and N326.

In further accordance with this invention, such tire is provided having an electrical path of least electrical resistance extending from a mounting surface of a rubber component in the bead portion of the tire to the running surface of the tire rubber cap layer.

In particular, said electrical path of least electrical resistance extends from the mounting surface of an electrically conductive rubber component in the bead region of the tire to said electrically conductive cord, optionally through an intermediate electrically conductive rubber component contiguous with said mounting surface-containing rubber component, thence to either said electrically conductive tread base rubber layer or through said electrically conductive rubber of said belt ply to said tread base rubber layer, thence to the running surface of said tire rubber cap layer via said tire rubber cap layer or, optionally, via said thin rubber strip which optionally extends through or around said tread rubber cap layer to at least a portion of the running surface thereof and wherein said electrically conductive cord is exclusive of an outer surface of said tire.

In practice, said additional rubber composition(s) of said tire bead region which is (are) relatively electrically conductive may be in a form of a tire chafer, chipper and/or toe guard and such components for a tire bead portion of the tire are well known to those having skill in such art. Conventionally, the tire chafer and toe guard components are both relatively electrically conductive, are contiguous with each other and, together, have a tire wheel-rim tire mounting surface. At least one of said additional rubber compositions is contiguous to another so there is a continuous path of relative electrical conductivity extending from said electrically conductive cord to the mounting surface of at least one of said additional rubber composition(s).

Thus, in practice, at least one of said additional rubber compositions of said tire bead portion provides a mounting surface of the tire where said mounting surface is adapted to contact a metal rim to form a tire/rim assembly. Usually, it is the tire chafer and toe guard, if used, which provide a tire mounting surface for mounting the tire on a rigid metal rim.

In practice, the aforesaid rubber reinforcing carbon blacks typically used for tire sidewall rubber compositions as earlier described, and therefore the said outer rubber sidewall layer of this invention, are usually of a somewhat larger particle size than carbon blacks conventionally used for tire tread rubber cap layer compositions. Such carbon blacks for reinforcing tire sidewall rubber compositions are, for example, those with ASTM designations of N550, N326 and N330. Rubber compositions containing these types of carcass grade rubber reinforcing carbon blacks typically require a content of at least 50 phr of the carbon black in the respective rubber composition to be suitably electrically conductive.

Alternatively, however, a blend of rubber reinforcing carbon blacks may be used for the sidewall layer such as, for example, at least two of N550, N326 and N375 carbon blacks.

In practice, it is preferred that at least 50 percent of the rubber reinforcing carbon black for said outer sidewall rubber layer is comprised of the aforesaid rubber reinforcing carbon blacks having ASTM designation of N550, N375 or N326.

As hereinbefore presented, while the tire tread rubber base layer is of a carbon black-rich rubber composition of a relatively high electrical conductivity, the outer tread rubber cap rubber layer may be of either a carbon black-rich rubber composition of relatively high electrical conductivity or a carbon black deficient (low carbon black content) rubber composition and therefore having a relatively low electrical conductivity.

If the tread cap layer is of a relatively low electrical conductivity, then a means is typically provided for a path of increased electrical conductivity to extend from the carbon black-rich tread base layer to the outer running surface of the tread rubber cap layer intended to be ground contacting. Such means may be, for example, the aforesaid thin rubber strip (e.g. from about 0.2 to about 5 mm wide) of a carbon black-rich rubber composition which extends through or around the tread rubber cap layer to at least a portion of its running surface.

Accordingly, where the tire tread outer cap rubber layer having an outer running surface is relatively electrically nonconductive, a means is provided for a path of reduced electrical resistivity to extend from said carbon black-rich tread belt ply layer to the outer running surface of said tread cap layer. Said means of providing a path of reduced electrical resistivity may be provided, for example, by the aforesaid thin rubber strip of a carbon black-rich rubber composition which contains at least 50 phr of carbon black wherein said thin rubber strip is positioned through, or around a portion of, the tread rubber cap layer to extend from a running surface of said tread cap layer to

(A) said carbon black-rich rubber tread base layer, or to

(B) an additional carbon black-rich rubber composition in contact with said tread base layer;

wherein the rubber composition of said tread base layer and said additional rubber composition in contact with said base layer contains at least 50 phr of carbon black.

Therefore, for example, such means of providing a path of reduced electrical resistivity is said thin rubber strip of a carbon black-rich rubber composition which contains at least 50 phr of carbon black positioned through, or around a portion of, the tread rubber cap layer to extend from a running surface of said tread cap layer to said carbon black-rich rubber tread base layer, wherein said rubber compositions of said individual tire bead component(s), said tire tread rubber base layer, said tire belt ply, and said thin rubber strip extending through or around said tread rubber cap layer contains a rubber reinforcing carbon black content in a sufficient amount that is above the carbon black percolation point to thereby make said rubber compositions relatively electrically conductive.

BRIEF DESCRIPTION OF THE DRAWINGS

Drawings are provided herewith as FIGS. 1 through 4 which illustrate positioning of an electrically conductive cord comprised of a metal filament spirally wrapped around a core of at least one organic fiber filament.

FIG. 1 depicts a cross-section of a portion of an open toroidally shaped pneumatic tire with the electrically conductive cord positioned between a carcass ply and outer sidewall rubber layer and FIG. 2 depicts a perspective view of a cross-section of the pneumatic tire with FIG. 1 being a somewhat more detailed drawing of the tire construction.

FIG. 3 depicts a cross-section of a portion of an open toroidally shaped pneumatic tire with the electrically conductive cord positioned between a carcass ply and an innerliner rubber layer and FIG. 4 depicts a perspective view of a cross-section of the pneumatic tire with FIG. 3 being a somewhat more detailed drawing of the tire construction.

THE DRAWINGS

Referring to FIG. 1, FIG. 2, FIG. 3 and FIG. 4, and particularly FIG. 1, cross-sections of an open toroidally shaped tire (1) are presented with two spaced apart bead regions (2), a rubber chafer/toe guard component(s) as additional components (3) as a part of the bead regions (2).

The rubber chafer/toe guard component (3) provides a mounting surface (3A) for mounting the tire on a rigid metal wheel-rim (not shown) to form an enclosed, air-containing cavity.

The Figures further depict a circumferential rubber tread component (4) of a cap/base construction, outer rubber sidewalls (5) extending radially outward from said bead region(s) (2) and associated rubber chafer/toe guard component(s) (3) to and connecting with the peripheral edges of the tread (4) of the tire (1), together with one or more cord reinforced rubber carcass plies (11), wherein the carcass plies extend from bead portion-to-bead portion through the crown portion (14) of the tire (1) and where the carcass plies (11) support the rubber sidewalls (5) and ultimately the circumferential tread (4) and belt plies (12).

The Figures depict a circumferential belt ply (12) underlying and supporting said tread component (4) composed of a rubber composition reinforced with steel cords.

In the Figures, the tire sidewall (5) is shown as being composed of an outer visible rubber layer (6).

In FIG. 1 and FIG. 2, and particularly FIG. 1, an electrically conductive cord (7) is shown as being positioned on the outer surface of the carcass ply (11) and thereby on the inside of the rubber sidewall layer (6) namely between the carcass ply (11) and outer sidewall rubber layer (6) extending from the rubber chafer/toe guard components (3) of the bead region(s) (2) to and connecting with the rubber coating of the rubber coated belt ply (12) juxtapositioned to the tread rubber base layer (8) of said tread component (4) and exclusive of the outer, exposed surface of the outer sidewall layer (6) where the electrically conductive cord (7) overlays the carcass ply (11) and is therefore next to said outer sidewall layer (6). The cord (7) is thereby actually positioned between the carcass ply (11) and the rubber sidewall (6). In this case the rubber of the carcass ply (11) may be relatively electrically non-conductive or electrically conductive.

In FIG. 3 and FIG. 4, particularly FIG. 3, the electrically conductive cord (7) is shown as being positioned on an inner surface of the carcass ply (11) and therefore between the carcass ply (11) and tire innerliner (13) in a manner that it extends from the bead regions through a crown region, or portion, (14) of the tire to thereby provide a path of least electrical resistance therebetween. In this case, the rubber of the carcass ply (11) is intended to be relatively electrically conductive in order to provide a path of least electrical resistance through the carcass ply (11) to the rubber coating of the belt ply (12).

Alternately, (not shown) the electrically conductive cord (7) may be positioned as an integral cord of the carcass ply (11) and therefore extending from the tread portion and a bead portion to thereby provide a path of least electrical resistance therebetween. In this case, the rubber of the carcass ply (11) is intended to be relatively electrically conductive in order to provide a path of least electrical resistance between through the carcass ply (11) to the rubber coating on the belt ply (12).

The electrically conductive cord (7) is composed of a fine electrically conductive stainless steel wire filament which is spirally (helically) wound around a core of at least one polyester fiber.

In FIG. 2, the internal electrically conductive cord (7) is shown as extending from bead component of one bead region to bead component of the other bead region (2) through the crown region (14) of the tire.

For the drawings, the outer sidewall layer (6) is of a rubber composition having a relatively low electrical conductivity (a relatively high electrical volume resistivity of at least 1.0E10 ohm-cm) and the rubber compositions of the chafer (3), tread base layer (8) and belt ply (12) have a relatively high electrical conductivity.

Accordingly, it is seen herein that the internal electrically conductive cord (7) provides a path of increased electrical conductivity (reduced electrical resistance) between said chafer component (3) with its running surface (3A) of the bead region (2) of the tire and the belt ply (12) and the associated tire tread base layer (8).

It can be seen that the internal electrically conductive cord (7) does not physically extend to and is therefore exclusive of and not a part of, the outer visible surface (9) of the tread cap layer, or running surface of the tread (10) intended to be ground-contacting or component (3) of the bead region (2) having a mounting surface (3A). In practice, the internal electrically conductive cord (7) does not physically extend to the tread cap layer (10) and therefore preferably does not extend to the running surface (10) of the tire (1) and, also, does not extend to the mounting surface (3A) of the tire and thereby does not actually contact the wheel rim (not shown) onto which the tire is to be mounted. Indeed, it is the indicated carbon black-rich rubber compositions themselves which make contact with the ground (the running surface of the tread cap layer) and which are the tire mounting surface thereby complete the electrical path of reduced electrical resistivity between the tire mounting surface and tire running surface.

If the tread cap layer (10) rubber composition contains only a minimal content of carbon black reinforcement, such as for example, a silica-rich rubber composition which is primarily reinforced with precipitated silica, in a manner that the tire tread cap layer (10) rubber composition has a relatively low electrical conductivity, then a means may be provided to extend the path of electrical conductivity to the ground-contacting outer surface (9) of the tread cap layer (10) such as by, for example, providing a thin extension of the electrically conductive tread base layer (8) through the tread cap layer (10) to its outer surface (9) intended to be ground-contacting or around a portion of the tread cap layer (10) via a thin carbon black-rich rubber strip of a relatively electrically conductive rubber composition extending from a tire component adjacent to said outer surface (9) of said tread cap layer (10) of a carbon black-rich rubber composition of a relatively high electrical conductivity which is a part of or is in contact with said tread base layer (8).

It is envisioned herein said the aforesaid carbon black content of said outer sidewall layer causes the outer sidewall layer to have a significantly reduced electrical conductivity relative to said tire bead, chafer and tread components. It is therefore envisioned herein that the positioning of the said electrically conductive cord between the outer sidewall layer and carcass ply provides a path of increased electrical conductivity (reduced electrical resistance) between said chafer component and belt ply component and associated tread base layer component. It is further envisioned herein that such positioned electrically conductive cord provides a path of increased electrical conductivity (reduced electrical resistance) whether or not the outer sidewall rubber layer is relatively electrically conductive or electrically non-conductive.

As hereinbefore pointed out, various particulate rubber reinforcing carbon blacks conventionally used for reinforcement of various tire component rubber compositions are referenced in the Vanderbilt Rubber Handbook (1978), Pages 414 through 417.

A significant aspect of this invention is the providing a path of increased electrical conductivity (and path of least electrical resistance) extending between the bead portion(s) and tread portion of the tire via the positioned electrically conductive cord.

As hereinbefore discussed, such electrically conductive cord may be positioned, for example, on an outer surface of a carcass ply and thereby between the carcass ply and outer rubber sidewall.

As hereinbefore discussed, alternately, the electrically conductive cord may be positioned, for example, on an inner surface of a carcass ply and thereby between the carcass ply and a tire rubber innerliner wherein the rubber composition of the carcass ply is relatively electrically conductive.

As hereinbefore discussed, alternately, the electrically conductive cord may be positioned, for example, as a cord contained in the cord reinforced rubber carcass ply wherein the rubber composition of the carcass ply is relatively electrically conductive.

This is considered herein as being significant to provide such path of increased electrical conductivity, and thereby least electrical resistance, between the tire bead component and tire tread component, without actually extending to the tire tread component's running surface or the tire bead component's mounting surface (relying upon appropriate carbon black reinforced, relatively electrically conductive rubber compositions contained in the bead component and tire tread component to extend the path of reduced electrical resistance to the tire running surface and tire mounting surface) to aid in reducing static electricity build up within the tire or tire/rim assembly.

In practice the organic fiber core of the cord may be comprised of at least one filament of various organic fibers, particularly synthetic fibers, such as, for example and not intended to be limiting, aramid, nylon, rayon, polyester, ultra high molecular weight polyethylene (UHMWPE) or cotton or blend of such fibers.

In practice the electrically conductive metal filament spirally (helically) wound around the core may be of various metals, and alloys thereof, such as for example, steel (an iron alloy and including stainless steel), copper and brass.

In practice the diameter of the core of the cord is preferably significantly greater than the diameter of the metal filament(s).

It is readily understood by those having skill in the art that the rubber compositions of the respective components of the tire would be compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable constituent rubbers with various commonly used additive materials such as, for example, curing aids, such as sulfur, activators, retarders and accelerators, processing additives, resins including tackifying resins, and plasticizers, fillers, pigments, fatty acid, zinc oxide, waxes, antioxidants and antiozonants and reinforcing materials such as, for example, carbon black. As known to those skilled in the art, depending on the intended use of the sulfur vulcanizable and sulfur vulcanized material (rubbers), the additives mentioned above are selected and commonly used in conventional amounts.

Typical amounts of tackifier resins, if used, may comprise about 0.5 to about 10 phr, usually about 1 to about 5 phr. Typical amounts of processing aids may comprise 1 to 20 phr. Such processing aids are intended to exclude, or at least substantially exclude aromatic, naphthenic, and/or paraffinic processing oils. Typical amounts of antioxidants comprise about 1 to about 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in the Vanderbilt Rubber Handbook (1978), Pages 344 through 346. Typical amounts of antiozonants comprise about 1 to about 5 phr. Typical amounts of fatty acids, if used, which can include stearic acid comprise about 0.5 to about 3 phr. Typical amounts of zinc oxide comprise about 2 to about 6 phr. Typical amounts of waxes comprise about 1 to about 5 phr. Often microcrystalline waxes are used. Typical amounts of peptizers comprise about 0.1 to about 1 phr. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide. The presence and relative amounts of the above additives are considered to be not an aspect of the present invention unless otherwise indicated.

The vulcanization is conducted in the presence of a sulfur vulcanizing agent. Examples of suitable sulfur vulcanizing agents include elemental sulfur (free sulfur) or sulfur donating vulcanizing agents, for example, an amine disulfide, polymeric polysulfide or sulfur olefin adducts. Preferably, the sulfur vulcanizing agent is elemental sulfur. As known to those skilled in the art, sulfur vulcanizing agents are used in an amount ranging from about 0.5 to about 4 phr, with a range of from about 0.5 to about 2.25 being preferred.

Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used, i.e., primary accelerator. Conventionally, a primary accelerator is used in amounts ranging from about 0.5 to about 2.0 phr. In another embodiment, combinations of two or more accelerators which the primary accelerator is generally used in the larger amount (0.5 to 2 phr), and a secondary accelerator which is generally used in smaller amounts (0.05 to 0.50 phr) in order to activate and to improve the properties of the vulcanizate. Combinations of these accelerators have been known to produce a synergistic effect on the final properties and are somewhat better than those produced by use of either accelerator alone. In addition, delayed action accelerators may be used which are not affected by normal processing temperatures but produce satisfactory cures at ordinary vulcanization temperatures. Suitable types of accelerators that may be used in the present invention are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. Preferably, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound. The presence and relative amounts of sulfur vulcanizing agent and accelerator(s) are not considered to be an aspect of this invention unless otherwise indicated.

Sometimes one or more of the antioxidants and antiozonants may be more simply referred to as antidegradants.

The tire can be built, shaped, molded and cured by various methods which will be readily apparent to those having skill in such art.

The prepared tire of this invention is conventionally shaped and cured by methods known to those having skill in such art.

EXAMPLE I

Tires of size P225/60R16 Eagle RS-A are prepared having treads of cap/base construction and constructed in a manner similar to FIG. 1 and FIG. 2 of the drawings insofar as the electrically relatively nonconductive rubber compositions of the carcass plies (11) and sidewall layer (6) are concerned, insofar as the electrically relatively conductive rubber compositions of the chafer component (3), with its tire mounting surface (3A), as well as the belt ply (12), tread base layer (8) and tread cap layer (9) are concerned.

Several spaced apart electrically conductive cords are placed to extend from bead-to-bead through the crown region of the tires. The electrically conductive cords are composed of a cord of polyester fibers, or filaments, around which was spirally (helically) wound a very thin stainless steel filament.

For a first tire, an electrically conductive cord (7) is positioned over a carcass ply (11), and thereby between the carcass ply (11) and rubber sidewall (6), and for which the cord (7) extends between (thereby connecting) the rubber chafer/toe guard component (3) of the tire bead region and rubber coat of the wire reinforced belt ply (12) in a manner similar to FIG. 1 and FIG. 2.

For a second tire, the electrically conductive cord (7), as depicted in FIG. 3 and FIG. 4), is positioned on the inside surface of the carcass ply (11), thereby between the carcass ply (11) and tire innerliner (13) which extends between the rubber chafer/toe guard component (3) and rubber coat of the wire reinforced belt ply (12).

The electrically conductive cord in each of the tires is exclusive of any outer, visually observable surface of the tire and is therefore exclusive of the tire mounting surface (3A) and tire running surface (10) as well as the visually exposed surface of the rubber sidewall (6).

Therefore, a path of least electrical resistance is provided between the tire mounting surface (3A) and tire running surface (10) which extends from the tire mounting surface (3A) through the rubber chafer/toe guard component (3), hence through the electrically conductive cord (7) to the rubber coat of the wire reinforced belt ply (12), hence to the tread rubber base layer (8), hence to the tread rubber cap layer (9) and its tire running surface (11).

The outer tire rubber sidewall layer (6), for the tire similar to FIG. 1, extending between said rubber chafer/toe guard component (3) of the bead portion and the tire tread rubber base layer (8) is composed of a relatively carbon black-deficient rubber composition comprised of natural cis 1,4-polyisoprene rubber and cis 1,4-polybutadiene rubber which contained only about 28 phr of N550 (ASTM designation) carbon black and is thus considered herein as being relatively electrically nonconductive.

The rubber composition of carcass ply (11) of synthetic cord reinforced rubber for the first tire (similar to FIG. 1 and FIG. 2) is composed of a relatively carbon black-deficient rubber composition comprised of natural cis 1,4-polyisoprene rubber only about 30 phr of N660 (ASTM designation) carbon black and is thus considered herein as being relatively electrically nonconductive.

The electrically conductive cord for the tires was comprised of a central core of synthetic polyester fibers around which was spirally (helically) wound a thin stainless steel filament.

The electrical resistance of the first tire (similar to FIG. 1) was determined by ASTM F1971-99 to be a value of about 1.4×10⁶ ohms, or about one megohm, between the mounting surface (3A) of the tire of the bead portion of the tire and the running surface (11) of the tire tread which is significantly less than a desired maximum resistance value of 1×10⁸ ohms, or 100 megohms.

For comparative purposes, a P225/60R16 tire was similarly prepared (similar to FIG. 1) but without the inclusion, or placement, of the electrically conductive cord (7). The electrical resistance of the tire was determined by ASTM F1971-99 to be a value of about 3.3×10⁸ ohms which is significantly greater than the above value of 1.4×10⁶ ohms obtained for the tires which contained the electrically conductive cords (7).

Accordingly, it is considered herein that the inclusion of the electrically conductive cord (7), particularly for the tire similar to FIG. 1, effectively provided a suitable electrical path of least electrical resistance between said rubber tire chafer/toe guard component (3) and the rubber of the wire reinforced rubber tire tread belt ply (12) and was a significant part of the electrical path extending from the tire rubber mounting surface (3A) and tire tread rubber running surface (11).

While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in this art that various changes and modifications may be made therein without departing from the spirit or scope of the invention. 

1. A pneumatic rubber tire of open toroidal shape comprised of: (A) a tire tread portion comprised of: (1) a circumferential rubber tread of a cap/base layered construction wherein said tread cap rubber layer has an outer tire tread running surface and said tread base rubber layer underlies said tread cap layer, and (2) a circumferential belt ply layer underlying said circumferential tread wherein said belt ply layer is comprised of steel cords encompassed by a rubber composition contiguous with said tread base rubber layer; (B) two spaced apart bead regions individually comprised of: (1) a bead portion comprised of relatively inextensible steel cords encompassed by a rubber composition, and (2) an additional bead portion comprised of at least one rubber component wherein at least one of said at least one additional bead portion rubber component has a mounting surface adapted for mounting said tire on a rigid metal rim, (C) at least one carcass ply comprised of a cord reinforced carcass ply rubber composition wherein at least one of said carcass plies extends from one bead portion to the other bead portion through the crown region of the tire, (D) a tire rubber inner liner layer positioned on the inside surface of an inner carcass ply, (E) two outer tire rubber sidewall layers individually extending between said bead region and said tread, and (F) at least one electrically conductive cord comprised of at least one electrically conductive metal filament spirally wound around a core of at least one organic fiber, wherein said at least one electrically conductive cord extends from the at least one of said at least one bead region additional rubber component as said at least one rubber component having a wheel-rim tire mounting surface and/or at least one intermediate rubber composition contiguous with said at least one wheel-rim mounting surface containing rubber component, to said tread rubber base layer, and/or said rubber of said circumferential belt ply wherein said at least one electrically conductive cord is positioned (1) on the outer surface of the outermost carcass ply between said carcass ply and said sidewall rubber layer, or (2) on the inner surface of the innermost carcass ply between said carcass ply and said tire rubber innerliner layer, or (3) between two carcass plies, or (4) as a member of said cords of at least one of said carcass plies; provided, however, that when said at least one electrically conductive cord is positioned between two carcass plies or between the innermost carcass ply and tire innerliner layer, or as a member of the cords of a carcass ply, (a) the said tread base layer, said tread belt ply, said tire bead composite, and said at least one additional bead component, and said carcass ply or plies are relatively electrically conductive by being comprised of carbon black-rich, rubber based rubber compositions having a relatively high electrical conductivity, and (b) the said outer sidewall rubber layer is: (1) relatively electrically conductive by being comprised of a carbon black rich rubber composition (2) relatively electrically non-conductive by being comprised of a rubber composition which contains only a minimal carbon black content or contains no carbon black provided however that when said at least one electrically conductive cord is positioned on the surface of the outermost carcass ply between said carcass ply and said outer sidewall layer, (c) the said tread base layer, tread belt ply, tire bead composite and at least one additional bead component are relatively electrically conductive by being comprised of carbon black-rich rubber compositions having a relatively high electrical conductivity, and (d) at least one of said carcass ply or plies and/or said outer sidewall rubber layer is: (1) relatively electrically conductive by being comprised of a carbon black rich rubber composition (2) relatively electrically non-conductive by being comprised of a rubber composition which contains only a minimal carbon black content or contains no carbon black); wherein the rubber composition of said tire tread rubber cap layer (e) is comprised of a carbon black-rich diene rubber based rubber composition thereby having a relatively high electrical conductivity, or (f) is comprised of a diene rubber based rubber composition which contains a more minimal carbon black content and thereby has a relatively low electrical conductivity; wherein a thin carbon black-rich rubber strip thereby having a relatively high electrical conductivity is positioned through or around said tread cap layer having the more minimal carbon black content and wherein said thin rubber strip extends from, and as a part of, said tread base rubber layer to at least a portion of the running surface of said tread cap layer; wherein the rubber composition of said outer rubber sidewall layer contains reinforcing filler as: (g) from about 50 to about 65 phr of rubber reinforcing carbon black, considered herein as being relatively electrically conductive, or (h) from about 25 to about 40 phr of rubber reinforcing carbon black, considered herein as being relatively electrically non-conductive, or (i) from about 25 to about 65 phr of amorphous, precipitated silica and from zero to 10 phr of rubber reinforcing carbon black, considered herein as being relatively electrically nonconductive, or (j) about 40 to about 70 phr of reinforcing filler as; (1) about 25 to about 40 phr of amorphous, precipitated silica and (2) about 25 to about 35 phr of rubber reinforcing carbon black, considered herein as being relatively non-electrically conductive; wherein a coupling agent is provided for said amorphous silica which has a moiety reactive with hydroxyl groups contained on said amorphous silica and another moiety interactive with said rubber; wherein said carbon black for said rubber sidewall layer has a dibutyl phthalate (DBP) value (ASTM D2414) in a range of from about 115 to about 125 cm³/100 g together with an Iodine value (ASTM D1510) in a range of from about 35 to about 50 ml/100 g; wherein the rubber composition of said carcass ply or plies contains reinforcing filler as: (k) about 45 to about 70 phr of rubber reinforcing carbon black, and is therefore considered herein as being relatively electrically conductive, or (l) from 25 to about 60 phr of reinforcing filler as; (1) from 5 to about 35 phr of carbon black, and (2) about 15 to about 55 phr of amorphous, precipitated silica together with a coupling agent for said silica and is therefore considered herein as being relatively electrically non-conductive; wherein said carbon black has a dibutyl phthalate (DBP) value (ASTM D2414) in a range of from about 70 to about 110 cm³/100 g together with an Iodine value (ASTM D1510) in a range of from about 30 to about 80 ml/100 g; wherein the rubber composition for said tread rubber cap layer contains reinforcing filler as: (m) about 45 to about 110 phr of rubber reinforcing carbon black, and is therefore considered herein as being relatively electrically conductive, or (n) from 45 to about 105 phr of reinforcing filler as; (1) from 5 to about 25 phr of carbon black, and (2) about 40 to about 100 phr of amorphous, precipitated silica together with a coupling agent for said silica and is therefore considered herein as being relatively electrically non-conductive; wherein said carbon black has a dibutyl phthalate (DBP) value (ASTM D2414) in a range of from about 110 to about 130 cm³/100 g together with an Iodine value (ASTM D1510) in a range of from about 85 to about 150 ml/100 g; wherein the rubber composition for said thin rubber strip extending through or around said tread rubber cap layer is of a carbon black-rich rubber composition, containing about 50 to about 75 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 100 to about 130 cm³/100 g together with an Iodine value in a range of from about 90 to about 125 ml/100 g; wherein the said at least one rubber composition of said at least one bead portion component having the said tire mounting surface contains from about 60 to about 125 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 70 to about 125 cm³/100 g together with an Iodine value in a range of from about 80 to about 145 ml/100 g, and is therefore considered herein as being relatively electrically conductive; wherein the rubber composition of said belt ply contains from about 55 to about 75 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 65 to about 85 cm³/100 g together with an Iodine value in a range of from about 75 to about 95 ml/100 g, and is therefore considered herein as being relatively electrically conductive; wherein the rubber composition of said tire tread rubber base layer contains from about 50 to about 70 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 90 to about 125 cm³/100 g together with an Iodine value in a range of from about 40 to about 95 ml/100 g, and is therefore considered herein as being relatively electrically conductive; wherein the rubber composition of said tire inner liner layer contains from about 55 to about 80 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 85 to about 95 cm³/100 g together with an Iodine value in a range of from about 30 to about 45 ml/100 g, and is therefore considered herein as being relatively electrically conductive.
 2. The tire of claim 1 wherein the rubber compositions of said at least one individual tire bead component, said tire tread rubber base layer, said tire belt ply, said optionally relatively electrically conductive tread rubber cap layer, said relatively electrically conductive outer sidewall layer, and said optional thin rubber strip extending through or around said tread rubber cap layer contain a rubber reinforcing carbon black content of at least 40 phr and in a sufficient amount that is above the carbon black percolation point.
 3. The tire of claim 1 wherein having an electrical path extending from said mounting surface of an electrically conductive rubber component in the bead region of the tire to said at least one electrically conductive cord, optionally through an intermediate electrically conductive rubber component contiguous with said mounting surface-containing rubber component, thence to either said electrically conductive tread base rubber layer or through said electrically conductive rubber of said belt ply to said tread base rubber layer, thence to the running surface of said tire rubber cap layer via said tire rubber cap layer or, optionally, via said thin rubber strip which optionally extends through or around said tread rubber cap layer to at least a portion of the running surface thereof and wherein said at least one electrically conductive cord is exclusive of an outer surface of said tire.
 4. The tire of claim 3 wherein said at least one electrically conductive cord extends from said at least one of said bead components to said circumferential belt ply component.
 5. The tire of claim 3 wherein said at least one electrically conductive cord extends from said at least one of said tire bead components to said tire tread base layer of said tire tread.
 6. The tire of claim 3 wherein said at least one electrically conductive cord extends from said at least one of said additional rubber composition components of at least one of said tire bead components to said tire tread.
 7. The tire of claim 3 wherein said at least one electrically conductive cord is comprised of at least one electrically conductive metal filament helically wound around a core of filaments selected from at least one of aramid, nylon, rayon, polyester and cotton fibers and wherein the diameter of the core of the cord is preferably significantly greater than the diameter of at least one the metal filament and wherein said at least one electrically conductive cord has an electrical resistance of less than 100 ohms.
 8. The tire of claim 1 wherein said at least one electrically conductive cord extends from said at least one tire bead component to said tire tread portion.
 9. The tire of claim 1 wherein said at least one electrically conductive cord extends from said at least one tire bead component to said circumferential belt ply component.
 10. The tire of claim 1 wherein said at least one electrically conductive cord extends from said at least one of said tire bead components to said tire tread component and thence to said other tire bead component.
 11. The tire of claim 1 wherein said at least one electrically conductive cord is positioned between the outermost carcass ply and said outer sidewall rubber layer.
 12. The tire of claim 1 wherein said at least one electrically conductive cord is positioned between two carcass plies.
 13. The tire of claim 1 wherein said at least one additional contiguous rubber composition of said tire bead components is a form of a tire chafer, chipper and/or toe guard.
 14. The tire of claim 1 wherein at least one of said contiguous rubber compositions of said tire bead components provides a mounting surface of the tire where said mounting surface is adapted to contact a metal rim to form a tire/rim assembly.
 15. The tire of claim 1 wherein said outer sidewall rubber layer contains from about 25 to about 35 phr of rubber reinforcing carbon black and, further, that at least 50 percent of the rubber reinforcing carbon black for said outer sidewall rubber layer is comprised of a carbon black having an ASTM designation of N550, N326 or N330; where said carbon black-rich rubber compositions for said tire bead, including said additional tire bead rubber compositions contain from about 70 to about 90 phr of carbon black, and wherein said electrically conductive cord has an electrical resistance of less than 100 ohms.
 16. The tire of claim 1 wherein said tire tread outer cap rubber layer has an outer running surface of the tire and said outer tread cap rubber layer is relatively electrically nonconductive and wherein a means is provided for a path of reduced electrical resistivity to extend from said carbon black-rich tread belt ply layer to the outer running surface of said tread cap layer, wherein said means of providing a path of reduced electrical resistivity is said thin rubber strip of a carbon black-rich rubber composition positioned through, or around a portion of, the tread rubber cap layer to extend from a running surface of said tread cap layer to (A) said carbon black-rich rubber tread base layer, or to (B) an additional carbon black-rich rubber composition in contact with said tread base layer.
 17. The tire of claim 16 wherein said means of providing a path of reduced electrical resistivity is said thin rubber strip of a carbon black-rich rubber composition positioned through, or around a portion of, the tread rubber cap layer to extend from a running surface of said tread cap layer to said carbon black-rich rubber tread base layer, wherein said rubber compositions of said at least one individual tire bead component, said tire tread rubber base layer, said tire belt ply, and said thin rubber strip extending through or around said tread rubber cap layer contains a rubber reinforcing carbon black content in a sufficient amount that is above the carbon black percolation point to thereby make said rubber compositions relatively electrically conductive.
 18. The tire of claim 1 wherein said at least one electrically conductive cord is comprised of said at least one electrically conductive metal filament helically wound around a core of filaments selected from at least one of aramid, nylon, rayon, polyester and cotton fibers and wherein the diameter of the core of the cord is preferably significantly greater than the diameter of the at least one metal filament.
 19. The tire of claim 1 wherein the carbon black for said tire bead portion rubber components is selected from at least one of N660, N550, N375, N236 and N234 carbon blacks; the carbon black for said tire tread rubber base layer is selected from at least one of N660, N555, N375 and N347 carbon blacks; the carbon black for said rubber of said belt ply is selected from at least one of N347, N330 and N326 carbon blacks; the carbon black for said tread rubber cap layer is selected from at least one of N375, N234, N220, N134, N121, N115 and N110 carbon blacks; the carbon black for said thin rubber strip which optionally extends through or around said tread rubber cap layer is selected from at least one of N375, N347 and N234 carbon blacks; the carbon black for said carcass ply rubber is selected from at least one of N660, N550 and N326 carbon blacks; the carbon black for said tire inner liner layer is a N660 carbon black; and the carbon black for said tire sidewall rubber layer is selected from at least one of N550, N660, N375, N330 and N326 carbon blacks.
 20. The tire of claim 1 wherein said at least one electrically conductive cord extends between said at least one of said bead component rubber compositions and said rubber of said circumferential belt ply and wherein said cord is positioned on the outer surface of the outermost carcass ply between said carcass ply and said sidewall rubber layer or on the inner surface of the innermost carcass ply between said carcass ply and said tire rubber innerliner layer.
 21. A pneumatic rubber tire of open toroidal shape is comprised of: (A) a tire tread portion comprised of: (1) a circumferential rubber tread of a cap/base layered construction wherein said tread cap rubber layer has an outer tire tread running surface and said tread base rubber layer underlies said tread cap layer, and (2) a circumferential belt ply layer underlying said circumferential tread wherein said belt ply layer is comprised of steel cords encompassed by a rubber composition contiguous with said tread base rubber layer; (B) two spaced apart bead regions individually comprised of: (1) a bead portion comprised of relatively inextensible steel cords encompassed by a rubber composition, and (2) an additional bead portion comprised of at least one rubber component wherein at least one of said at least one additional bead portion rubber component has a mounting surface adapted for mounting said tire on a rigid metal rim, (C) at least one carcass ply comprised of a cord reinforced carcass ply rubber composition wherein at least one of said carcass plies extends from one bead portion to the other bead portion through the crown region of the tire, (D) a tire rubber inner liner layer positioned on the inside surface of an inner carcass ply, (E) two outer tire rubber sidewall layers individually extending between said bead region and said tread, and (F) at least one electrically conductive cord comprised of at least one electrically conductive metal filament, electrically conductive carbon fiber, or their combination, spirally wound around a core of at least one organic fiber, wherein said at least one electrically conductive cord extends from the at least one of said at least one bead region additional rubber component as said rubber component having a wheel-rim tire mounting surface and/or at least one intermediate rubber composition contiguous with said at least one wheel-rim mounting surface containing rubber component, to said tread rubber base layer, and/or said rubber of said circumferential belt ply, wherein said at least one electrically conductive cord is positioned (1) on the outer surface of the outermost carcass ply between said carcass ply and said sidewall rubber layer, or (2) on the inner surface of the innermost carcass ply between said carcass ply and said tire rubber innerliner layer, or (3) between two carcass plies, or (4) as a member of said cords of at least one of said carcass plies; provided, however, that when said at least one electrically conductive cord is positioned between two carcass plies or between the innermost carcass ply and tire innerliner layer, of as a member or the cords of a carcass ply, (a) the said tread base layer, said tread belt ply, said tire bead composite, and said at least one additional bead component, and said carcass ply or plies are relatively electrically conductive by being comprised of carbon black-rich, rubber based rubber compositions having a relatively high electrical conductivity, and (b) the said outer sidewall rubber layer is: (1) relatively electrically conductive in a sense of being comprised of a carbon black rich rubber composition, or (2) relatively electrically non-conductive in a sense of being comprised of a rubber composition which contains only a minimal carbon black content or contains no carbon black; provided however that when said at least one electrically conductive cord is positioned on the surface of the outermost carcass ply between said carcass ply and said outer sidewall layer, (c) the said tread base layer, tread belt ply, tire bead composite and at least one additional bead component are relatively electrically conductive by being comprised of carbon black-rich rubber compositions having a relatively high electrical conductivity, and (d) at least one of said carcass ply or plies and/or said outer sidewall rubber layer is: (1) relatively electrically conductive in a sense of being comprised of a carbon black rich rubber composition, or (2) relatively electrically non-conductive in a sense of being comprised of a rubber composition which contains only a minimal carbon black content or contains no carbon black; wherein the rubber composition of said tire tread rubber cap layer (e) is comprised of a carbon black-rich diene rubber based rubber composition thereby having a relatively high electrical conductivity, or (f) is comprised of a diene rubber based rubber composition which contains a more minimal carbon black content and thereby has a relatively low electrical conductivity; wherein a thin carbon black-rich rubber strip thereby having a relatively high electrical conductivity is positioned through or around said tread cap layer having the more minimal carbon black content and wherein said thin rubber strip extends from, and as a part of, said tread base rubber layer to at least a portion of the running surface of said tread cap layer; wherein the rubber composition of said outer rubber sidewall layer contains reinforcing filler as: (g) from about 50 to about 65 phr of rubber reinforcing carbon black, considered herein as being relatively electrically conductive, or (h) from about 25 to about 40 phr of rubber reinforcing carbon black considered herein as being relatively electrically non-conductive, or (i) from about 25 to about 65 phr of amorphous, precipitated silica and from zero to 10 phr of rubber reinforcing carbon black considered herein as being relatively electrically nonconductive, or (j) about 40 to about 70 phr of reinforcing filler as; (1) about 25 to about 40 phr of amorphous, precipitated silica and (2) about 25 to about 35 phr of rubber reinforcing carbon blacks, considered herein as being relatively non-electrically conductive; wherein a coupling agent is provided for said amorphous silica which has a moiety reactive with hydroxyl groups (e.g. silanol groups) contained on said amorphous silica and another moiety interactive with said rubber; wherein said carbon black for said rubber sidewall layer has a dibutyl phthalate (DBP) value (ASTM D2414) in a range of from about 115 to about 125 cm³/100 g together with an Iodine value (ASTM D1510) in a range of from about 35 to about 50 ml/100 g; wherein the rubber composition of said carcass ply or plies contains reinforcing filler as: (k) about 45 to about 70 phr of rubber reinforcing carbon black, and is therefore considered herein as being relatively electrically conductive, or (l) from 25 to about 60 phr of reinforcing filler as; (1) from 5 to about 35 phr of carbon black, and (2) about 15 to about 55 phr of amorphous, precipitated silica together with a coupling agent for said silica and is therefore considered herein as being relatively electrically non-conductive; wherein said carbon black has a dibutyl phthalate (DBP) value (ASTM D2414) in a range of from about 70 to about 110 cm³/100 g together with an Iodine value (ASTM D1510) in a range of from about 30 to about 80 ml/100 g; wherein the rubber composition for said tread rubber cap layer contains reinforcing filler as: (m) about 45 to about 110 phr of rubber reinforcing carbon black, and is therefore considered herein as being relatively electrically conductive, or (n) from 45 to about 105 phr of reinforcing filler as; (1) from 5 to about 25 phr of carbon black, and (2) about 40 to about 100 phr of amorphous, precipitated silica together with a coupling agent for said silica and is therefore considered herein as being relatively electrically non-conductive; wherein said carbon black has a dibutyl phthalate (DBP) value (ASTM D2414) in a range of from about 110 to about 130 cm³/100 g together with an Iodine value (ASTM D1510) in a range of from about 85 to about 150 ml/100 g; wherein the rubber composition for said thin rubber strip extending through or around said tread rubber cap layer is of a carbon black-rich rubber composition, containing about 50 to about 75 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 100 to about 130 cm³/100 g together with an Iodine value in a range of from about 90 to about 125 ml/100 g; wherein the said at least one rubber composition of said at least one bead portion component having the said tire mounting surface contains from about 60 to about 125 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 70 to about 125 cm³/100 g together with an Iodine value in a range of from about 80 to about 145 ml/100 g, and is therefore considered herein as being relatively electrically conductive; wherein the rubber composition of said belt ply contains from about 55 to about 75 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 65 to about 85 cm³/100 g together with an Iodine value in a range of from about 75 to about 95 ml/100 g, and is therefore considered herein as being relatively electrically conductive; wherein the rubber composition of said tire tread rubber base layer contains from about 50 to about 70 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 90 to about 125 cm³/100 g together with an Iodine value in a range of from about 40 to about 95 ml/100 g, and is therefore considered herein as being relatively electrically conductive; wherein the rubber composition of said tire inner liner layer contains from about 55 to about 80 phr of rubber reinforcing carbon black having a dibutyl phthalate (DBP) value in a range of from about 85 to about 95 cm³/100 g together with an Iodine value in a range of from about 30 to about 45 ml/100 g, and is therefore considered herein as being relatively electrically conductive.
 22. The tire of claim 21 wherein said core of at least one organic fiber for said at least one electrically conductive cord is selected from at least one of aramid, nylon, rayon, polyester, ultra high molecular weight polyethylene, and cotton fibers, or their blend, and wherein the diameter of the core of the cord is preferably significantly greater than the diameter of the at least one metal filament and/or carbon fiber. 